2 1/2 inch plate supply 09cuptire-a stock

The use of low carbon steel is limited due to its low strength. The strength of the carbon steel can be greatly improved by properly increasing the manganese content in the supply 09CUPTIRE-A carbon steel and adding some alloy elements such as vanadium, titanium and niobium. If the carbon content in the carbon steel is reduced and a small amount of aluminum, boron and carbide forming elements are added, the ultra-low carbon bainite can be obtained, supply 09CUPTIRE-A which has high strength and good plasticity and toughness.

supply 09CUPTIRE-A, Grade P295GH chemical composition under EN10028-2:2003 is displayed as follows. Chemical composition (C: 0.08 to 0.20; Cr: ≤0.30; Si: ≤0.40; Cu: ≤0.30;Mn: 0.90 to 1.50; Mo: ≤0.08;P: ≤0.025; Nb: ≤0.020;S: ≤0.015; Ni: ≤0.30;Al: ≤0.020; Ti: 0.03; N: ≤0.012; Vi: ≤0.02). The yield Strength MPa (min) of P295GH steel plate with thickness less than 16mm is 295MPa, and the tensile strength is 460-580MPa.

Our quality and service commitment: supply 09CUPTIRE-A product quality problems, life-long replacement.In the process of using, any time if you find we supplied steel materials not conform to the requirements of technical standards, we can replace it for you free of charge. However, it should be noted that non product quality problems caused by improper use are not covered by the warranty. Please pay attention to the service time commitment as well as the product quality assurance commitment. Because only the products of big brands and reliable enterprises with complete after-sales service system can truly realize the long-term product quality assurance and the whole process of service.