1/4" high quality 05CuPCrNi weather resistant Hot Rolled, Steel Plate

Online sale hot rolled plate 3000 tons 05CUPCRNI weather resistant in Tianjin city50*2180*10000, 50*2500*12000, 50*2460*9250, 50*2440*9450, 50*2200*12003, 50*2200*12000, 50*2200*12004, 50*2430*7600, 50*2440*4200, 70*1620*7400, 50*2440*14200, 60*2500*7700, 50*2380*11400, 60*2500*10100, 66*2920*11000, 75*2000*8750, 50*2430*7700, 50*2200*11850, 70*1600*6000, 89*2600*6650, 50*2300*11600, 70*2920*8400, 100*2220*3050, 105*2560*7040.

Increasing the use of high-end steel will help reduce carbon emissions. The use of high-strength, high-toughness, corrosion-resistant and wear-resistant, fatigue-resistant, and long-life steel materials should be increased; on the basis of meeting the requirements for the use of steel products, the integrated application of structural lightweight design, lightweight materials, and lightweight manufacturing technologies should be realized; Improve the yield rate of steel and optimize the steel recycling system.

Its weatherability is the protection of the oxide layer of weatherproof steel. The mechanism of corrosion resistance of weathering steel is mainly based on the analysis of long-term exposed rust layer. Generally speaking, it is believed that weathering steel can form a dense layer of weathering rust through long-term exposure, which has a good protective effect on weathering steel, 05CUPCRNI weather resistant.

Hydrogen (H) is the most harmful element in general steel such as 05CUPCRNI weather resistant. Hydrogen dissolved in steel will cause hydrogen embrittlement, white spots and other defects. Hydrogen, like oxygen and nitrogen, has very little solubility in solid steel. It dissolves into liquid steel at high temperature, and accumulates in the structure without time to escape when cooling, forming high-pressure micro pores, which greatly reduce the plasticity, toughness and fatigue strength of steel, and even cause cracks and brittle fracture in severe cases. "Hydrogen embrittlement" mainly occurs in martensitic steel, but not very prominent in ferrite steel, and generally increases with hardness and carbon content.