Rolling process of grade 09CuPCrNi-B

The steel plate used for containers and pressure vessel has to bear different pressures and strengths due to the manufactured containers. The normal pressure is generally 31.4MPa or higher; the working temperature is usually between -20 ℃ -450 ℃, and sometimes lower than -20 ℃. According to the working conditions and processing technology of the container, the grade 09CUPCRNI-B, steel plate used for the container must have good cold bending and welding performance. Besides, it should have good plasticity and toughness, high temperature short-term strength or long-term strength performance.

Based on the grade 09CUPCRNI-B steel trade, the company mainly deals in Baosteel products: color coating, zinc plating, fingerprint resistance, cold rolling, hot rolling, pickling, electrical steel and other products, and can order the futures of the company's products on behalf of manufacturers. It has established cooperative relations with more than 2000 foreign customers. At the same time, it also operates a variety of products of related iron and steel enterprises. Annual sales of grade 09CUPCRNI-B steel 3.6 million tons, standing stock of 400000 tons, has developed more than 10000 users. The company has a first-class marketing service system, strong storage and transportation capacity and supporting supply, cutting distribution capacity, and gradually build it into an important marketing channel.

S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the grade 09CUPCRNI-B rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of grade 09CUPCRNI-B steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.

The effect of Q345B alloy steel plate on the mechanical properties in the annealed state. The strengthening effect of alloying elements on steel in the quenched and tempered state, because it fully utilizes all four strengthening mechanisms. Martensite is formed during quenching, and carbide is precipitated during tempering, resulting in a strong second-phase strengthening, and at the same time greatly improving the toughness. Therefore, obtaining martensite and tempering it is an economical and effective comprehensive strengthening method for steel such as grade 09CUPCRNI-B.

Adhere to the spirit of quality first and user foremost, carry out maintenance and other work according to the requirements of the buyer's contract, and ensure that the engineering project and product after-sales play their application effectiveness. Our company guarantees to carry out self inspection and self supervision according to the quality management policy proposed by our company, and deliver a high-grade, perfect and excellent system engineering to users.